Laser/Inkjet Printable Polyester Film

This specification is intended to outline the physical and chemical properties of PANDUIT’s pressure sensitive laser and inkjet

printable polyester material and include the following part numbers and printable material identifiers:

Part Number Prefixes

Printable Material Suffixes

LJSL*Y

Y*J

PLL

PRODUCT SPECIFICATIONS:

Description:

Material is RoHS compliant (European Union directive 2002/95/EC).

Material is top coated to provide a laser/inkjet printable surface. This

material is halogen free.

Print Methods:

This material is recommended for laser and inkjet printing.

Adhesive:

Acrylic based, pressure sensitive permanent adhesive.

Standard Colors:

Clear with colored print-on area

Thickness:

2.0 +/- 0.3 mils (substrate and adhesive)

Service Temperature Range:

-65°F to 225°F (-54°C to 107°C)

Minimum Application Temperature:

50°F (10°C)

Storage Conditions:

Store at 70°F (21°C) and 50% Relative Humidity.

PROPERTIES:

PERFORMANCE:

Peel Adhesion to Stainless Steel:

35 oz/in width (PSTC-101, 15 min. dwell)

Shear Adhesion:

24+ hours (PSTC-107, Procedure A)

Tensile Strength:

MD 56lbs/ inch width +/- 15% (ASTM D882)

TD 72 lbs/inch width +/- 15% (ASTM D882)

Elongation:

MD 160% +/- 15% (ASTM D882)

TD 120% +/- 15% (ASTM D882)

Elevated Temperature Exposure:

After 8 hours at 275°F (135°C) there was no deterioration of the substrate

Tack:

470 g/cm

2 (ASTM D-2979-71, 1 sec dwell)

Immersion Resistance:

Printed samples were applied to stainless steel panels and immersed in “Isopar

‘L’ and Isopar ‘M’ solutions to determine if the printing would smear or if the

adhesive would degrade.

Immersion Time

Visual Changes

10 minutes

None

30 minutes

None

60 minutes

None

24 hours

None

UV Resistance:

*3000 hours equates to 5 years of assimilated

Outdoor UV exposure.

*3000 hours no change observed (ASTM G154)