Normal Wall, Flexible

Halogen-Free Polyolefin Heat Shrink Tubing

Newark.com/multicomp-pro

Farnell.com/multicomp-pro

sg.element14.com/b/multicomp-pro

Characteristics:

•  Halogen Free

•  Operating temperature -55°C to +125°C

•   Min. shrink temperature 70°C 

Full recovery temperature: 120°C

•  Shrink Ratio 2:1

•  Meets Sony-SS-00259

•  Standard Colours: Black, Red, Yellow, White, Blue, Brown

Applications

The heat shrink tubing is manufactured with modified radiation cross-linked polyolefin. The 

specially designed halogen free formulation makes the tubing very flexible and shrink at lower 

temperature. Suitable for applications where temperature sensitive components protection, 

e.g. PVC jacketed wire and cable and quick shrinkage is required. It has good mechanical and 

electrical performances.

Technical Data:

Property

Test Method

Standard Value

Tensile Strength

ASTM D2671

≥10.4 Mpa

Ultimate Elongation

ASTM D2671

≥200%

Longitudinal Shrinkage

UL 224

±5%

Heat Aging 

Tensile Strength 

Ultimate Elongation

158°C, 168hrs

≥7.3 Mpa

≥100%

Heat shock

250°C, 4hrs

No cracking, No dripping

Flammability

FMVSS302

Pass

Dielectric Strength

ASTM D150

≥15 kV/mm

Volume Resistivity

ASTM D2671

≥1x1014    Ωcm

Copper Stability

UL224

Pass

Copper Corrosion

UL224

No corrosion

Product Dimensions:

Size

As supplied

After Recovery

Inch

mm

Internal diameter

(mm)

Wall thickness

(mm)

Internal diameter

Max(mm)

Wall thickness

Nom(mm)

1/16

1.6

1.5 ±0.2

0.2 ±0.05

0.65

0.36 ±0.1

3/32

2.4

2.5 ±0.2

0.2 ±0.05

1

0.45 ±0.1

1/8

3.2

3.5 ±0.2

0.2 ±0.05

1.5

0.45 ±0.1

3/16

4.8

5 ±0.2

0.28 ±0.05

2.3

0.56 ±0.1