DP8010 Blue • DP8010NS Blue

Page 3

Temperature

3M™ Scotch-

Weld™ Structural

Plastic Adhesive

DP8010 Blue

3M™ Scotch-

Weld™ Structural

Plastic Adhesive

DP8010NS Blue

-20°F (-29°C)

2000 mixed

2000 mixed

73°F (23°C)

1800 CF

1700 CF

120°F (49°C)

1000 mixed

700 mixed

150°F (66°C)

450 AF

340 AF

180°F (82°C)

300 AF

100 AF

6. Overlap shear values measured using ASTM D1002; adhesives allowed to cure for 7 days at room temperature;

½” overlap; 0.010” bond line thickness; samples pulled at 0.1 in/min for metals and 2 in/min for plastics; all

surfaces prepared with light abrasion and solvent clean; substrates used were 1/16” thick aluminum and 1/8” thick

plastics; failure modes: AF: adhesive failure CF: cohesive failure SF: substrate failure mixed: AF/CF

Substrate

3M™ Scotch-

Weld™ Structural

Plastic Adhesive

DP8010 Blue

3M™ Scotch-

Weld™ Structural

Plastic Adhesive

DP8010NS Blue

Aluminum (MEK/abrade/MEK)

1960 CF

1780 CF

Cold-rolled steel

(MEK/abrade/MEK)

1800 CF

1870 CF

Stainless Steel (MEK/abrade/MEK)

1820 CF

1990 CF

Copper (MEK/abrade/MEK)

1870 CF

1500 CF

Galvanized steel (

MEK/abrade/MEK)

1330 CF

840 mixed

PP (IPA wipe)

1150 SF

1150 SF

LDPE (IPA wipe)

360 SF

360 SF

HDPE (IPA wipe)

1040 SF

1100 SF

UHMW-PE (IPA wipe)

770 CF

750 SF

Gelcoat (fiberglass--smooth side)

900 SF

1100 SF

Acrylic

1100 SF

1190 SF

PVC

1730 SF

1740 SF

PC

760 AF

740 AF

ABS

1250 SF

1240 SF

Polystyrene (HIPS)

580 SF

570 SF

FRP (Epoxy)

2830 CF

2860 CF

Acetal

90 AF

70 AF

SMC (Fiberglass--rough side)

760 SF

800 SF

Glass

530 SF

670 SF

PTFE (IPA/abrade/IPA)

320 AF

360 AF

Note: The following technical information and data should be considered

representative or typical only and should not be used for specification

purposes.

Typical Cured

Physcial

Properties

(continued)